Just another WordPress site - Ruhr-Universität Bochum

In the present work we investigate three mechanical and microstructural aspects of high temperature and low stress creep of the single crystal superalloy LEK 94. First, we compare the tensile creep behavior of specimens loaded in precise [001] and [110] directions and show that tensile creep specimens with precise [110] directions show significantly lower minimum creep rates. However, small deviations from precise [110] orientations result in a significant increase of creep rate. Second, we use a novel SEM technique to measure dislocation densities. We show that after short periods of creep, dislocation densities in dendritic regions are always higher than in interdendritic regions. This finding is probably associated with wider γ-channels, higher concentrations of W and Re and higher misfit stresses in the γ-channels of dendrites. Finally, we show that internal stresses associated with solidification can drive complex rafting processes during high temperature exposure, which differ between dendrite cores and interdendritic regions.